Mainly used in graphite anode, graphite flume, graphite mold processing and graphite plate and other fields, with dense and uniform structure, high temperature resistance, oxidation resistance, low resistivity, high density characteristics.
Maximum granularity：0.8mm
Specification：Special specifications can be custom-made and processed.
| Fine-Grain Graphite FXG-1 | |||
| Item | Units | Guarantee Values | Typical Values |
| Max.Grain size | mm | 0.8 | 0.8 |
| Bulk Density | g/cm³ | ≥1.70 | 1.73 |
| Specific Resistance | μΩ·m | ≤8.5 | 7.5 |
| Flexural Strength | MPa | ≥10.0 | 11.0 |
| Compressive Strength | MPa | ≥24.0 | 27.0 |
| Thermal Conductivity | W/(m·K) | ≥120 | 150 |
| C.T.E.(100 to 600℃） | 10-6/℃ | ≤2.5 | 2.2 |
| Ash Content | % | ≤0.3 | 0.09 |
| Fine-Grain Graphite FXG-2 | |||
| Item | Units | Guarantee Values | Typical Values |
| Max.Grain size | mm | 0.8 | 0.8 |
| Bulk Density | g/cm³ | ≥1.73 | 1.76 |
| Specific Resistance | μΩ·m | ≤8.0 | 7 |
| Flexural Strength | MPa | ≥12.0 | 12.5 |
| Compressive Strength | MPa | ≥31.0 | 34.0 |
| Thermal Conductivity | W/(m·K) | ≥130 | 160 |
| C.T.E.(100 to 600℃） | 10-6/℃ | ≤2.5 | 2.1 |
| Ash Content | % | ≤0.3 | 0.09 |
| Medium-Grain Graphite FCP | |||||||
| Item | Units | Guarantee Values | Typical Values | Guarantee Values | Typical Values | Guarantee Values | Typical Values |
| Max.Grain size | mm | 2 | 2 | 4 | 4 | 8 | 8 |
| Bulk Density | g/cm³ | ≥1.58 | 1.6 | ≥1.57 | 1.58 | ≥1.56 | 1.58 |
| Specific Resistance | μΩ·m | ≤11.5 | 10.5 | ≤11.5 | 10.5 | ≤12.5 | 11.5 |
| Flexural Strength | MPa | ≥6.0 | 6.5 | ≥6.5 | 7.0 | ≥7.0 | 7.5 |
| Compressive Strength | MPa | ≥18.0 | 18.5 | ≥17.5 | 18.0 | ≥16.0 | 17.0 |
| Elastic Modulus | GPa | ≤9.3 | 7.5 | ≤9.3 | 7.5 | ≤9.3 | 7.0 |
| C.T.E.(100 to 600℃） | 10-6/℃ | ≤2.5 | 2.4 | ≤2.5 | 2.4 | ≤2.5 | 2.4 |
| Ash Content | % | ≤0.3 | 0.09 | ≤0.3 | 0.09 | ≤0.3 | 0.09 |
| Medium-Grain Graphite FCG-1 | |||||||
| Item | Units | Guarantee Values | Typical Values | Guarantee Values | Typical Values | Guarantee Values | Typical Values |
| Max.Grain size | mm | 2 | 2 | 4 | 4 | 8 | 8 |
| Bulk Density | g/cm³ | ≥1.70 | 1.75 | ≥1.69 | 1.73 | ≥1.68 | 1.72 |
| Specific Resistance | μΩ·m | ≤8.5 | 7.5 | ≤8.5 | 7.5 | ≤9.0 | 8.5 |
| Flexural Strength | MPa | ≥9.0 | 9.5 | ≥9.5 | 10.0 | ≥10.0 | 12.5 |
| Compressive Strength | MPa | ≥30.0 | 31.0 | ≥29.0 | 30.0 | ≥30.0 | 31.0 |
| Elastic Modulus | GPa | ≤12.0 | 9.5 | ≤12.0 | 9.5 | ≤12.0 | 9.0 |
| C.T.E.(100 to 600℃） | 10-6/℃ | ≤2.5 | 2.3 | ≤2.5 | 2.3 | ≤2.5 | 2.3 |
| Ash Content | % | ≤0.3 | 0.09 | ≤0.3 | 0.09 | ≤0.3 | 0.09 |